Lightweight Clay Insulating Brick be used as inner lining brick of industry kilns wall and industry furnance at working Temperature °C: > 1200 . The Lightweight Clay Insulating Brick is made of high purity fire clay, by adding combustible, gas evolution method, or foam method. Lightweight fire brick is a kind of porous material with Al2O3 content 30-46%.
Its refractoriness is 1580-1750 ℃, refractoriness under load is 1250-1450 ℃, with good thermal resistance and strong ability to resistant acid slag.The bulk density is 0.75-1.2g/cm3, crushing strength is 2.0-5.9MPa, thermal conductivity is 0.221-0.442W/(m.K) (1350℃)
Lightweight Clay Insulating Brick can not be in direct contact with the flame.
Product Characteristics:
- Low levels of iron and other impurities
- High refractoriness,but can not contact with the flame directly
- High porosity, low volume density, low thermal conductivity
- Good heat insulating effect and energy-efficient
- Good thermal shock stability.
- Corrosion and erosion resistance
- Long service life
Performance parameters：
|
Item |
Lightweight Clay Insulating Brick |
|||
|
0. 6 |
0.8 |
1.0 |
1.3 |
|
|
Al2O3 (%) |
40 |
40 |
40 |
40 |
|
Fe2O3 (%) |
1.5 |
1.5 |
1.2 |
2 |
|
SiO2 |
55 |
55 |
55 |
55 |
|
Bulk Density (g/cm3) |
0.6 |
0.8 |
1.0 |
1.3 |
|
Apparent Porosity % |
70 |
60 |
55 |
50 |
|
Cold Crushing Strength(Mpa) ≥≥ |
2.0 |
2.5 |
3.0 |
4.0 |
|
Reheating Linear Change (%) ℃ X 12H ≤ |
1300℃ -0.5 |
1350℃ -0.5 |
1350℃ -0.9 |
1350℃ -0.9 |
|
Thermal Conductivity(W/m.k)(1000℃) |
0.33 |
0.60 |
0.45 |
0.8 |
|
Max Service Temperature (℃) |
1200 |
1280 |
1300 |
1350 |
| General specification | |
| Applications: | Lightweight Clay Insulating Brick can be used as inner lining brick of industry kilns wall and industry furnance.such as blast furnace, hot blast stoves ,electric arc furnace,cement kiln,melting furnace,ignition furnace,flue,refining equipment,heating equipment and piping, regeneration device, gas furnace,soaking furnace,annealing furnace,heat reaction chamber and other thermal industrial equipment. |
| Temperature resistance °С | 1250-1450 ℃ |
| Weight: | 0.75-1.2g/cm3 |
Applications
- Industrial Kilns
- Furnaces
- Nuclear Applications
FAQ
What is the maximum working temperature of the Lightweight Clay Insulating Brick?
What is the Al2O3 content range in the Lightweight Clay Insulating Brick?
Can the Lightweight Clay Insulating Brick be in direct contact with flame?
Lightweight Clay Insulating Brick
- Brand: GTeek
- Product Code: Lightweight Clay Insulating Brick
- Availability: ✅On stock
Available Options
Related Products
Light Weight Mullite Insulation Brick
Light Weight Mullite Insulation Brick Light Weight Mullite Insulation Brick, mainly based on aluminum silicate-based refractory materials, with some excellent performance, (especially high temperature creep performance) living in natural raw materials production Of the high aluminum products first. Mullite composition AL203 in about 79%, Si02 in 21% is more appropriate, but there are a certain amount of raw materials in the impurity composition, at high temperatures wil..
High-Alumina Brick - up to 1735°C - 20mm thickness
Description A、Refractoriness 20mm high-alumina brick Refractoriness is higher than Clay brick and semi-silica brick,reaching 1750~1790℃，it’s the advanced refractory materials. B、Refractoriness under load The high alumina products is in the high Al2O3, less impurities, the formation of fusible glass less, so the load softening temperature than the clay brick, but the mullite crystallization doesn’t form a network organizations, therefore refractoriness under load ..
Tags: Lightweight, Clay, Insulating, Brick