Polyamide 6 sheets - oil filled
Nylon 6 Oil Filled Yellow sheets is an engineering plastic with product characteristics including excellent sliding properties, self-lubricating, and improved "stick-slip" properties.
Oil Filled Polyamide: A special formulation of liquid lubricant encapsulated during manufacture provides for true lubrication at the bearing surface. This is cast nylon with built-in oil lubrication. During the manufacturing process, oil lubrication is completely and evenly dispersed throughout the cast nylon 6, making it an integral part of the material’s structure that cannot spin out, dry out, or drain out, even under the harshest working conditions.
This oil-filler reduces the friction of the oil-filled Nylon 6 sheet by as much as 25% at the bearing interface and can result in longer wear life than unfilled or moly-filled cast nylons. The standard grade is yellow in color, but a natural (off-white) colored FDA & USDA approved grade is also available
The long term service temperature range of the oil-filled Nylon 6 sheet is from -40°C to 85°C and has a short term maximum service temperature of 160°C. Typical fields of application for oil-filled Nylon 6 sheet include mechanical engineering, packing industry and conveyor industries, machine parts, bearings, bushings, gears, valve seats and wear surfaces, rollers, guides.
Oil-filled Nylon 6 sheet is a material well suited to CNC turning, bulletin, and precision grinding. Similar materials available from us include Nylon 6 Cast Natural Rod and Acetal C Extruded Natural Rod. If you have a requirement for machined or finished Oil filled Nylon 6 sheets components please ask our team for more information.
| MECHANICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Modulus of elasticity (tensile test) |
3100 | MPa | 1mm/min | DIN EN ISO 527-2 |
| Tensile strength | 70 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Tensile strength at yield | 68 | MPa | 50mm/min | DIN EN ISO 527-2 |
| Elongation at yield | 4 | % | 50mm/min | DIN EN ISO 527-2 |
| Elongation at break | 50 | % | 50mm/min | DIN EN ISO 527-2 |
| Flexural strength | 95 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Modulus of elasticity (flexural test) |
2900 | MPa | 2mm/min, 10 N | DIN EN ISO 178 |
| Compression strength | 21/37/78 | MPa | 1% / 2% / 5% | EN ISO 604 |
| Compression modulus | 2700 | MPa | 5mm/min, 10 N | EN ISO 604 |
| Impact strength (Charpy) | n.b. | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eU |
| Notched impact strength (Charpy) | 6 | kJ/m2 | max. 7,5J | DIN EN ISO 179-1eA |
| Ball indentation hardness | 150 | MPa | ISO 2039-1 |
| THERMAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Glass transition temperature | 42 | C | DIN EN ISO 11357 | |
| Melting temperature | 216 | C | DIN EN ISO 11357 | |
| Service temperature | 170 | C | short term | NN |
| Service temperature | 100 | C | long term | NN |
| Thermal expansion (CLTE) | 13 | 10-5*1/K | 23-60°C, long. | DIN EN ISO 11359-1;2 |
| Thermal expansion (CLTE) | 13 | 10-5*1/K | 23-100°C, long. | DIN EN ISO 11359-1;2 |
| Specific heat | 1.7 | J/(g*K) | ISO 22007-4:2008 | |
| Thermal conductivity | 0.37 | W/(k*m) | ISO 22007-4:2008 |
| ELECTRICAL PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| surface resistivity | 1014 | O | DIN IEC 60093 | |
| volume resistivity | 1014 | O*cm | DIN IEC 60093 |
| OTHER PROPERTIES | VALUE | UNIT | PARAMETER | NORM |
|---|---|---|---|---|
| Resistance to hot water/ bases | (+) | - | - | |
| Flammability (UL94) | HB | - | corresponding to | DIN IEC 60695-11-10; |
| Resistance to weathering | - | - | - | |
| Water absorption | 0.4 | % | 24h / 96h (23°C) | DIN EN ISO 62 |
| General specification | |
| Applications: | mechanical engineering, packing industry and conveyor industries, machine parts, bearings, bushings, gears, valve seats and wear surfaces, rollers, guides. |
| Temperature resistance °С | -40°C +85°C, shortly +160°C |
| Weight: | 1.14 g/cm³ |
| Color | yellow, white, green, black |
| Technical datasheet | Polyamide 6 sheets - oil filled |
Applications
- Industrial Machinery
- Automotive Components
- Marine Applications
FAQ
What are the main benefits of using oil filled polyamide?
How is the oil lubrication integrated into the polyamide?
Can oil filled polyamide be used in high-temperature environments?
Polyamide 6 sheets - oil filled
- Brand: Germany
- Product Code: Polyamide 6 sheets - oil filled
- Availability: On stock
Available Options
Related Products
Polyamide 6 sheets
Polyamide PA6 sheets Polyamide 6 (PA 6) also called Nylon 6 is the most common polyamide which offers a balanced combination of all typical characteristics of this group of materials. Damping properties and impact strength of the material deserve to be emphasized as much as high tenacity even at low temperatures. Compared to the types with fillers, PA 6 / Nylon 6 sheets have a higher moisture absorption, are less wear-resistant, and are slightly..
Polyamide 66 sheets
(PA 66) Polyamide 66 sheets have good rigidity, hardness, abrasion resistance and thermal dimensional stability. With respect to these particular aspects, PA66 offers certain advantages compared to PA 6. Compared to the cast types, PA 66 has higher moisture absorption. With regard to all other characteristics, PA 66 is comparable to the standard cast type PA 6 G, but more expensive. Characteristics of Polyamide 66 sheets: good mechanical ..
Polyamide 6 MoS2 sheets
Polyamide 6 MoS2 sheets Polyamide 6 MoS2 sheet comes in black color. The addition of Molybdenum Sulphide (MoS2) to PA6 results in an increase of rigidity, hardness and dimensional stability due to its nucleating effect. Conversely, the material's impact strength is reduced as a result. The additive also lends the material improved sliding friction properties. High rigidity High degree of hardness Good dimensional stability Lower impact s..
Polyamide 12 sheets
Polyamide 12 sheets Polyamide 12 sheets have good wear resistance and good sliding properties. It has a very low density among all engineering plastics (1.02 g / cm3). A very durable polymer that can withstand high static and dynamic loads. The distinguishing feature of Polyamide 12 plates - low water absorption, which is typically very high for all other polyamides, which reduces the mechanical, electrical, and thermal characteristics. Polyamide 12 sheets&nbs..